vaccum casting clear parts
vaccum casting clear parts vaccum casting
![](//v4-upload.goalsites.com/515/1623917280_image.png)
Adhibition
VACUUM INJECTION POLYURETHANE RESIN FOR MAKING HIGH TEMPERATURE RESISTANT PROTOTYPE PARTS
Characteristic
•Good refractory
•simplicity of operator
•Easy coloring •High replication accuracy
operational process(Use a vacuum casting machine)
>After stirring, tilt the cup and defoaming for 1-2 minutes;
>Put stingy, pour the material into the preheated 50-60° C silicone mold;
>Put the mold into the oven at 70° C to cure for 60 minutes and then release the mold.
Dongguan zhongda model technology co., LTD. New research and development of a new type of transparent plastic model, is in hot sale, the following pictures, please look forward to the next exciting.
![](http://v4-upload.goalsites.com/515/1623917280_image.png)
Adhibition
VACUUM INJECTION POLYURETHANE RESIN FOR MAKING HIGH TEMPERATURE RESISTANT PROTOTYPE PARTS
Characteristic
•Good refractory
•simplicity of operator
•Easy coloring •High replication accuracy
physical performance | |||
ingredient | UP 6160-LSPOLYOL | UP 6160-LISOCYANATE | MDS |
polyhydric alcohols | isocyanate | ||
重量混合比 | 100 | 200 | |
appearance | liquid state | liquid state | liquid state |
colour | faint yellow | colourless | faint yellow |
appearance | liquid state | liquid state | liquid state |
Brockfield has a viscosity of 23℃(mPa.s) | 300-400 | 200-300 | 200-300 |
Density is zero before mixing 25℃ (g/cm)After curing, the density is at 23℃ (g/cm3) | 0.96-1.01 | 1.20-1.23 | 1.2 |
operable time (100g)于20-25℃ (minute) | 6.8 |
operational process(Use a vacuum casting machine)
>Weigh the two components according to the ratio,Place the isocyanate component in the top cup;
>After 5-10 minutes of defoaming in vacuum injection machine,Pour the isocyanate into the polyol and stir for 1 minute.>After stirring, tilt the cup and defoaming for 1-2 minutes;
>Put stingy, pour the material into the preheated 50-60° C silicone mold;
>Put the mold into the oven at 70° C to cure for 60 minutes and then release the mold.
Mechanical properties - at 23 ° C (1) | ||
hardness | Shore D | 80-81 |
Modulus of elasticity in bending | MPa | 2100-2200 |
Bending strength | MPa | 108- 128 |
tensile strength | MPa | 59-69 |
And elongation at fracture | % | 15-16 |
Impact strength (1ZOD) notch specimen | J/M | 34-44 |
Dongguan zhongda model technology co., LTD. New research and development of a new type of transparent plastic model, is in hot sale, the following pictures, please look forward to the next exciting.